POLYMERS
ABS
•• AG1000
•• AG12A0
•• AG15A0 
•• AG15E0
•• AG12A1
•• AG15A1
•• AG15A2
••  AG15E1
•• AG12AJ
•• AG15AJ
•• AT5900 
•• AF3500
•• AF3600
•• AX4000
•• AX4100
•• AX4300
•• AG22AT 
•• AT5500 
•• AH2003
•• AG10NP 
•• AG10AP 
•• AE8000 
•• AE8200
•• ANC100 
•• ANC120
EVA
HDPE
LDPE
LLDPE
PP
PVC
POM

TEXTILE INDUSTRIES
Polyester & Nylon Chips

Polyester & Nylon Yarn
High Tenacity Industrial Yarns
Spun Yarns

Polyester & Viscose Fiber
Belting Fabrics
Tyre Cord Fabrics

BOTTLE INDUSTRIES
Polyester Chips

ELECTRONICS & ELECTRICAL

FOOD INDUSTRIES
Spices
Dry Fruits

 


Acrylonitrile Butadiene Styrene ( ABS ) -AT5900
 
Specification

Property Unit Test Method Test Condition  AT5900
Tensile Strength kg/cm2 ASTM D-638 23℃ 500
( MPa) ( ISO527) -49
Flexural Strength kg/cm2 ASTM D-790 23℃ 900
( MPa) ( ISO178) -89
Flexural Modulus kg/cm2 ASTM D-790 23℃ 30000
( MPa) ( ISO178) -2950
Rockwell R-Scale ASTM D-785 23℃ R-119
Hardness ( ISO2039/2 )
Izod kg-cm/cm ASTM D-256 23℃ 6
Impact Strength ( J/m ) ( ISO R180 ) 1/4'' bar -59
Vicat Softening ASTM D-1525  1Kg load 102
Temperature (ISO 306)
Heat Deflection ASTM D-648 Unannealed 87
Temperature (ISO 75/A) 18.6kg/cm2
    ( 1/2'' bar )
    Annealed 99
    ( 80℃×8Hr )
Melt  g/10 min ASTM D-1238 220℃×10Kg 18
Flow Index ( ISO1133 ) ( 98N )
Pencil Scratch   ASTM D-3363 750g weight H
(JIS K5600-5-4)
Molding  % FCFC Method 23℃ 0.4~0.7
Shrinkage
Specific Gravity   ASTM D-792 23℃/23℃ 1.05
( ISO1183 )
Flammability    UL-94 FILE NO. 1/16" HB
E162823 All Color


 