POLYMERS
ABS
•• AG1000
•• AG12A0
•• AG15A0 
•• AG15E0
•• AG12A1
•• AG15A1
•• AG15A2
••  AG15E1
•• AG12AJ
•• AG15AJ
•• AT5900 
•• AF3500
•• AF3600
•• AX4000
•• AX4100
•• AX4300
•• AG22AT 
•• AT5500 
•• AH2003
•• AG10NP 
•• AG10AP 
•• AE8000 
•• AE8200
•• ANC100 
•• ANC120
EVA
HDPE
LDPE
LLDPE
PP
PVC
POM

TEXTILE INDUSTRIES
Polyester & Nylon Chips

Polyester & Nylon Yarn
High Tenacity Industrial Yarns
Spun Yarns

Polyester & Viscose Fiber
Belting Fabrics
Tyre Cord Fabrics

BOTTLE INDUSTRIES
Polyester Chips

ELECTRONICS & ELECTRICAL

FOOD INDUSTRIES
Spices
Dry Fruits

 



Acrylonitrile Butadiene Styrene ( ABS ) -AG15A1
 
 
Specification

Property
Unit
Test Method Test Condition    G15A1
Tensile Strength
kg/cm2
ASTM D-638
23°C
510
( MPa)
( ISO527)
-50
Flexural Strength
kg/cm2
ASTM D-790
23°C
850
( MPa)
( ISO178)
-83
Flexural Modulus
kg/cm2
ASTM D-790
23°C
27000
( MPa)
( ISO178)
-2650
Rockwell
R-Scale
ASTM D-785
23°C
R-110
Hardness ( ISO2039/2 )
Izod
kg-cm/cm
ASTM D-256
23°C
20
Impact Strength
( J/m )
( ISO R180 )
1/4'' bar
-196
Vicat Softening
°C
ASTM D-1525 
1Kg load
104
Temperature (ISO 306)
Heat Deflection
°C
ASTM D-648
Unannealed
89
Temperature (ISO 75/A)
18.6kg/cm2
   
( 1/2'' bar )
   
Annealed
101
   
( 80°C×8Hr )
Melt 
g/10 min
ASTM D-1238
200°C×5Kg
1.6
Flow Index ( ISO1133 )
( 49N )
   
220°C×10Kg
17
   
( 98N )
Molding 
%
FCFC
23°C
0.4~0.7
Shrinkage Method
Specific Gravity
ASTM D-792
23°C/23°C
1.05
( ISO1183 )
Flammability   
UL-94
FILE NO.
1/16" HB
E162823
All Color


 