ABS
•• AG1000
•• AG12A0
•• AG15A0 
•• AG15E0
•• AG12A1
•• AG15A1
•• AG15A2
••  AG15E1
•• AG12AJ
•• AG15AJ
•• AT5900 
•• AF3500
•• AF3600
•• AX4000
•• AX4100
•• AX4300
•• AG22AT 
•• AT5500 
•• AH2003
•• AG10NP 
•• AG10AP 
•• AE8000 
•• AE8200
•• ANC100 
•• ANC120
EVA
HDPE
LDPE
LLDPE
PP
PVC
POM

TEXTILE INDUSTRIES
Polyester & Nylon Chips

Polyester & Nylon Yarn
High Tenacity Industrial Yarns
Spun Yarns

Polyester & Viscose Fiber
Belting Fabrics
Tyre Cord Fabrics

BOTTLE INDUSTRIES
Polyester Chips

ELECTRONICS & ELECTRICAL

FOOD INDUSTRIES
Spices
Dry Fruits

 



Acrylonitrile Butadiene Styrene ( ABS ) -AG12A0
 
Specification

Property Unit Test Method
Test Condition
 AG12A0
Tensile Strength kg/cm2 ASTM D-638
23℃
510
( MPa) ( ISO527) -50
Flexural Strength kg/cm2 ASTM D-790
23℃
750
( MPa) ( ISO178) -74
Flexural Modulus kg/cm2 ASTM D-790
23℃
25000
( MPa) ( ISO178) -2450
Rockwell R-Scale ASTM D-785
23℃
R-106
Hardness ( ISO2039/2 )
Izod kg-cm/cm ASTM D-256
23℃
30
Impact Strength ( J/m ) ( ISO R180 )
1/4'' bar
-294
Vicat Softening ASTM D-1525 
1Kg load
103
Temperature (ISO 306)
Heat Deflection ASTM D-648
Unannealed
88
Temperature (ISO 75/A)
18.6kg/cm2
   
( 1/2'' bar )
   
Annealed
100
   
( 80℃×8Hr )
Melt  g/10 min ASTM D-1238
200℃×5Kg
1.6
Flow Index ( ISO1133 )
( 49N )
   
220℃×10Kg
17
   
( 98N )
Molding  % FCFC Method
23℃
0.4~0.7
Shrinkage
Specific Gravity   ASTM D-792
23℃/23℃
1.04
( ISO1183 )
Flammability    UL-94
FILE NO.
1/16" HB
E162823
All Color


 